电镀，抗弯曲，照明装置，良好的表面光洁度

VESTODUR® X9420

聚丁烯对苯二甲酸酯

Evonik Degussa GmbH

 

Technical Data

 

产品说明

 

Polybutylene terephthalate compounds for headlight bezels with low fogging even at high operating temperatures

 

VESTODUR X9420

Non-reinforced, easy flowing compound with an increased amount of mold release agent

 

The mentioned compounds are semicrystalline thermoplastic compounds based on PBT, all suitable for injection molding. Even at temperatures up to 160°C, they exhibit very little gassing, therefore being best suited to manufacture parts like headlight bezels. The VESTODUR® compounds recommended here make it possible to manufacture complex, precisely fitting headlight geometries, giving designers more freedom in their designs.

 

Textured, mostly black or gray bezel surfaces are also possible. The finished headlight bezels resist warpage and are thermally stable. Their surfaces can at any rate be metallized in the high surface quality required by the automotive industry, even when textured.

 

The fogging behavior can be tested by the „Fogging test" according to DIN 75201. High fogging values (>90 %) mean low outgassing behavior.

 

总体

 

材料状态 • 实验阶段：进行中

资料 1 •  Technical Datasheet (English)

搜索 UL 黄卡 •  VESTODUR®

供货地区 • 北美洲 • 欧洲

添加剂 • 脱模

• Low to No Fogging • 电镀 • 良好的流动性

性能特点 • 半结晶 • 抗弯曲 • 热稳定性，良好

• 除气作用低至无 • 良好的表面光洁度 • 脱模性能良好

用途 • 电气/电子应用领域 • 汽车领域的应用： • 照明装置

外观 • 黑色 • 灰色

形式 • 颗粒料

加工方法 • 注射成型

物理性能 额定值单位制 测试方法

密度 1.31g/cm³ ISO 1183

溶化体积流率（MVR） (250°C/2.16 kg) 48.0cm³/10min ISO 1133

收缩率 3 ISO 294-4

横向流量: 80°C, 2.00 mm 2.0%

流量: 80°C, 2.00 mm 1.8%

吸水率 (饱和, 23°C) 0.50% ISO 62

机械性能 额定值单位制 测试方法

拉伸模量 2700MPa ISO 527-2

拉伸应力 (屈服) 60.0MPa ISO 527-2

拉伸应变 ISO 527-2

屈服 8.0%

断裂 15%

冲击性能 额定值单位制 测试方法

简支梁缺口冲击强度 ISO 179/1eA

-30°C, 完全断裂 4.0kJ/m²

23°C, 完全断裂 4.0kJ/m²

简支梁缺口冲击强度 ISO 179/1eU

-30°C, 完全断裂 120kJ/m²

23°C, 完全断裂 140kJ/m²

硬度 额定值单位制 测试方法

支撐硬度 (邵氏 D) 77 ISO 868

 

 

VESTODUR® X9420

聚丁烯对苯二甲酸酯

Evonik Degussa GmbH

热性能 额定值单位制 测试方法

热变形温度

0.45 MPa, 未退火 185°C ISO 75-2/B

1.8 MPa, 未退火 65.0°C ISO 75-2/A

维卡软化温度

-- 220°C ISO 306/A

-- 190°C ISO 306/B

线形膨胀系数 ISO 11359-2

流动: 23 到 55°C 0.00010cm/cm/°C

横向: 23 到 55°C 0.00010cm/cm/°C

电气性能 额定值单位制 测试方法

表面电阻率 1.0E+14ohm IEC 60093

体积电阻率 1.0E+13ohm•cm IEC 60093

耐电强度 4 27kV/mm IEC 60243-1

相对电容率 IEC 60250

100 Hz 3.30

1 MHz 5.50

耗散因数 IEC 60250

100 Hz 0.0015

1 MHz 0.021

漏电起痕指数 IEC 60112

解决方案 A 5 575V

解决方案 A 600V

可燃性 额定值单位制 测试方法

UL 阻燃等级 UL 94

0.800 mm HB

1.60 mm HB

补充信息 额定值单位制 测试方法

Electrolytical Corrosion - Step A1 IEC 60426

Outgassing - Fogging-value 6 (150°C) 93% DIN 75201

 

 

 

 

 

 

Evonik Degussa GmbH聚丁烯对苯二甲酸酯,Evonik Degussa GmbH PBT,PBT VESTODUR® X9420塑料是东莞市双帮塑胶原料有限公司常年销售的塑料，因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表、SGS报告，ROHS报告，REACH报告  SVHC报告，COA出厂报告,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123  微信：13549213581     联系电话：13549213581肖生