ASTADUR™ B4300G6-UV    
    
聚丁烯对苯二甲酸酯    
    
Marplex Australia Pty. Ltd.   
     
 Technical Data    
     

产品说明

ASTADUR™ B4300G6 is a 30% glass fibre reinforced, UV stabilized grade of polybutylene terephthalate (PBT) polymer. It has excellent processability, high rigidity and heat resistance and is resistant to chemical attack. It is suitable for applications where rigidity and heat resistance are of high importance.

Note: The letters "UV" or "W" indicate UV stabilisation has been added [ ie: ASTADUR™ B4300G6UV ].

总体

 材料状态  • 已商用：当前有效   
 资料 1  •  Technical Datasheet (English)
  
 Search for UL Yellow Card •  Marplex Australia Pty. Ltd.
  
 供货地区  • 北美洲 • 南美洲 • 亚太地区 
 填料/增强材料 • 玻璃纤维增强材料, 30% 填料按重量  
 添加剂  • 紫外线稳定剂   
 性能特点  • 刚性，高 • 耐热性，中等  
   • 可加工性，良好 • 中等硬度  
      
      
 物理性能   额定值单位制 测试方法 
 比重   1.53g/cm³ ASTM D792 
 熔流率 (250°C/2.16 kg)  14g/10 min ASTM D1238 
 收缩率 - 流动 (3.00 mm)  0.30 到 0.70% ASTM D955 
 吸水率 (饱和)  0.35% ASTM D570 
 机械性能   额定值单位制 测试方法 
 抗张强度 3 (3.20 mm)  125MPa ASTM D638 
 伸长率 3 (断裂, 3.20 mm)  2.0% ASTM D638 
 弯曲模量 4 (3.20 mm)  6800MPa ASTM D790 
 弯曲强度 4 (3.20 mm)  170MPa ASTM D790 
 冲击性能   额定值单位制 测试方法 
 悬壁梁缺口冲击强度 (3.20 mm)  60J/m ASTM D256 
 硬度   额定值单位制 测试方法 
 洛氏硬度 (R 计秤)  112 ASTM D785 
 热性能   额定值单位制 测试方法 
 热变形温度   ASTM D648 
 0.45 MPa, 未退火, 3.20 mm  220°C  
 1.8 MPa, 未退火, 3.20 mm  215°C  
 维卡软化温度  220°C ASTM D1525 5 
 线形膨胀系数 - 流动  0.000020 到 0.000030cm/cm/°C ASTM D696 
 可燃性   额定值单位制 测试方法 
 UL 阻燃等级 (1.60 mm)  HB UL 94 
 热灯丝点火温度 (1.60 mm)  550°C AS/NZS 60695 
      
 注射   额定值单位制  
 干燥温度   100 到 120°C  
 干燥时间   4.0 到 6.0hr  
 螺筒后部温度  230 到 240°C  
 加工（熔体）温度  250 到 270°C  
 模具温度   90.0°C  
 注塑温度   60.0 到 140MPa  
 注射速度   快速  
 背压   0.300 到 1.00MPa  
 合模力   4.0 到 8.0kN/cm²