CBT® 200
聚丁烯对苯二甲酸酯
Cyclics Corporation 

Technical Data

产品说明

CBT® 200 resin melts to a water-like viscosity when heated, then polymerizes into the engineering thermoplastic polybutylene terephthalate (PBT). CBT 200 resin has a processing range between 170-240°C and is available in both one and two-part systems. CBT 200 resin is formulated for various casting, low pressure molding, coatings and composite applications where the lower melt temperature allows for longer working time than CBT 100 resin before polymerizing into PBT.

CBT 200 resin has a melt temperature of 165°C (329°F) which is 15°C (37°F) lower than Cyclics CBT 100 resin.

总体

材料状态 • 已商用：当前有效   
供货地区 • 北美洲 • 欧洲  
性能特点 • 耐化学性良好 • 耐气候影响性能良好  
 • 耐酒精 • 耐碳氢化合物  
     
形式 • 颗粒料   
加工方法 • 浇铸 • 注射成型  
     
物理性能   额定值 单位制 测试方法 
比重   1.31g/cm³ ASTM D792 
收缩率 - 流动 (4.00 mm)   1.5% ASTM D955 
机械性能   额定值 单位制 测试方法 
拉伸模量   2700MPa ISO 527-2 
拉伸应力 (屈服)   54.0MPa ISO 527-2 
拉伸应变    ISO 527-2 
屈服   3.2%  
断裂   50%  
弯曲模量   2380MPa ISO 178 
弯曲强度   74.0MPa ISO 178 
冲击性能   额定值 单位制 测试方法 
悬壁梁缺口冲击强度 (23°C)   6.7kJ/m² ISO 180/1A 
无缺口伊佐德冲击强度 (23°C)   无断裂 ISO 180/1U 
热性能   额定值 单位制  
熔融温度   165°C  
可燃性   额定值 单位制 测试方法 
UL 阻燃等级 (4.00 mm)   HB UL 94 
充模分析   额定值 单位制 测试方法 
熔体密度   1.14g/cm³  
熔体粘度    ASTM D3835 
170°C, 10.0 sec^-1   0.0370Pa•s  
180°C, 10.0 sec^-1   0.0280Pa•s  
190°C, 10.0 sec^-1   0.0220Pa•s  
200°C, 10.0 sec^-1   0.0170Pa•s  
210°C, 10.0 sec^-1   0.0130Pa•s  
220°C, 10.0 sec^-1   0.0110Pa•s  
补充信息     
Solid Heat Capacity, ASTM E1269: 1.25 J/g.°C   
Liquid Heat Capacity, ASTM E1269, 180°C (356°F): 1.96 J/g.°C   
Heat of Melting, ASTM E793: 64 J/g     
     
注射   额定值 单位制  
加工（熔体）温度   230 到 260°C  
模具温度   180 到 200°C